West Kalimantan is a region with a high potential for bauxite resources; therefore, the bauxite processing industry generates a significant amount of waste. The waste produced includes bauxite tailings and fly ash. This research method consists of material characteristic testing, mix design planning based on SNI 7656-2012, specimen preparation, and testing of the specimens. This study aims to analyze the effect of using bauxite tailings waste and fly ash as substitutes for fine aggregate (sand) and cement on the physical and mechanical properties of normal concrete. The variations of bauxite tailings used were 10%, 15%, and 20%, with fly ash content fixed at 5% in each mixture. The results show that the third variation, which used 10% bauxite tailings and 5% fly ash, achieved the highest compressive strength of 36.712 MPa at the age of 28 days.
Kalimantan Barat merupakan wilayah dengan potensi sumber bauksit yang cukup tinggi sehingga dari proses pengolahan bauksit tersebut menghasilkan jumlah limbah yang cukup besar. Limbah yang dihasilkan tersebut diantarannya adalah limbah tailing bauksit dan fly ash. Metode penelitian ini meliputi pengujian karakteristik material, perencanaan campuran berdasarkan SNI 7656-2012, pembuatan benda uji, serta pengujian pada benda uji. Penelitian ini bertujuan untuk menganalisis pengaruh penggunaan limbah tailing bauksit dan abu terbang (fly ash) sebagai bahan subsitusi pasir dan semen terhadap sifat fisis dan mekanis beton normal,variasi tailing bauksit yang digunakan adalah 10%,15%, dan 20%, serta fly ash sebanyak 5% pada setiap campuran. Hasil penelitian ini menunjukan kuat tekan variasi ke-3 yaitu dengan penggunaan limbah tailing bauksit 10% dan abu terbang (fly ash) 5% dengan kuat tekan sebesar 36,712 MPa pada umur 28 hari.
References
[1] Ashad, H., Supardi, S., Mappiasse, A., Muh Ikram Zhahir, A., & Prabowo Surya, D. (2020). Pemanfaatan Limbah Pembakaran Batu Bara sebagai Bahan Subsitusi Parsial Semen.
[2] Ayu Ginting, N., Nirmala, A., & Hendri Sutrisno, dan. (2023). Analisis Pengaruh Penambahan Tailing Bauksit sebagai Agregat Halus pada Pembuatan Paving Block Di PT. Anugerah Borneo Maruya Persada. In Jurnal Teknologi Lingkungan Lahan Basah (Vol. 11, Number 02).
[3] Darmawan, M., Isram, M., Ain, M., Achmad, K., Teknik, M. T. J., Politeknik, S., & Balikpapan, N. (n.d.). PENAMBAHAN FLY ASH SEBAGAI BAHAN CAMPURAN BETON NORMAL.
[4] Fitri Febrianti, R., Anita Zaharah, T., Jurusan Kimia, A., & Unversitas Tanjungpura, F. (2022). SINTESIS ZEOLIT A BERBAHAN DASAR ABU TERBANG (FLY ASH) LIMBAH PT. INDONESIA CHEMICAL ALUMINA (ICA) MENGGUNAKAN METODE ALKALI HIDROTERMAL (SYNTHESIS OF ZEOLITE A BASE ON FLY ASH WASTE PT. INDONESIA CHEMICAL ALUMINA (ICA) USING HYDROTHERMAL ALKALINE METHOD). In / Indo. J. Pure App. Chem (Vol. 5, Number 1). http://jurnal.untan.ac.id/index.php/IJoPAC
[5] Hardjito, D. (2005). Faculty of Engineering and Computing Department of Civil Engineering Studies on Fly Ash-Based Geopolymer Concrete.
[6] Nasional, B. S. (2012). SNI-7656-2012 Tata cara pemilihan campuran untuk beton normal,beton berat dan beton massa. www.bsn.go.id
[7] Nasional, B. S. (2014). SNI-2460-2014-Spesifikasi Abu Terbang Batubara dan Pozolan.
[8] Nasional, B. S. (2015). SNI 2531:2015 Metode Uji Densitas Semen Hidraulid.
[9] Nasional Bandan Standarisasi. (2011). " Metode uji bahan organik dalam agregat halus untuk beton Standard Test Method for Organic Impurities in Aggregates for Concrete Badan Standardisasi Nasional. www.bsn.go.id
[10] Nurhayati, S., Shofiyani, A., & Zaharah, T. A. (2021). SINTESIS MAGNETIT DARI LIMBAH TAMBANG BAUKSIT MENGGUNAKAN TEMPLAT CETYLTRIMETHYLAMMONIUMBROMIDE. Jurnal Kimia Dan Kemasan, 43(2), 143. https://doi.org/10.24817/jkk.v43i2.6516
[11] Rabihati, E., Arief Purnama, I., Syafri Adjie, M., Dwi Rachmawan, V., Teknik Sipil, J., Negeri Pontianak, P., & Barat, K. (2020). PEMANFAATAN LIMBAH BAUKSIT (TAILING BAUXITE) SEBAGAI BAHAN PENGGANTI AGREGAT HALUS TERHADAP KUAT TEKAN, KUAT TARIK BELAH, DAN MODULUS ELASTISITAS PADA BETON (UTILIZATION OF BAUXITE (BAUXITE TAILING) AS A SUBSTITUTE FOR FINE AGGREGATE TO THE STRENGTH OF SPLIT TENSILE STRENGTH AND MODULUS OF ELASTICITY IN CONCRETE) (Vol. 1, Number 1).
[12] Spesifikasi Agregat Halus Untuk Pekerjaan Adukan Dan Plesteran Dengan Bahan Dasar Semen (2002).
[13] Surjarmiko, P. (2020). Prosiding Seminar Nasional Teknik Lingkungan Kebumian Ke-II Potensi Tailing Hasil Pencucian Bauksit Sebagai Pengganti Agregat Halus di Kabupaten Sanggau Kalimantan Barat. In Fakultas Teknologi Mineral.