Bauxite production in West Kalimantan is one of the largest in Indonesia. The bauxite processing process produces large amounts of waste, including red mud and bottom ash, which have the potential to cause negative impacts on the environment if not managed properly. Therefore, efforts are needed to utilize this waste, one of which is as a cement substitute in normal concrete. This research method includes testing material characteristics, concrete mix planning based on SNI standards, making test specimens, and testing compressive strength of concrete. This study aims to determine the effect of using red mud and bottom ash as partial cement substitutes on the compressive strength of normal concrete. The mixture variation used was bottom ash at 10% of the cement weight with variations in the addition of red mud at 0%, 5%, 10%, and 15%. The results showed that the addition of red mud and bottom ash affected the compressive strength of normal concrete, where the optimum mixture variation was obtained by using 10% bottom ash and 5% red mud which produced the highest compressive strength value compared to other variations.
Produksi bauksit di Kalimantan Barat merupakan salah satu yang terbesar di Indonesia. Proses pengolahan bauksit menghasilkan limbah dalam jumlah besar, di antaranya red mud dan bottom ash, yang berpotensi menimbulkan dampak negatif terhadap lingkungan apabila tidak dikelola dengan baik. Oleh karena itu, diperlukan upaya pemanfaatan limbah tersebut, salah satunya sebagai bahan substitusi semen pada beton normal. Metode penelitian ini meliputi pengujian karakteristik material, perencanaan campuran beton berdasarkan standar SNI, pembuatan benda uji, serta pengujian kuat tekan beton. Penelitian bertujuan untuk mengetahui pengaruh penggunaan red mud dan bottom ash sebagai bahan substitusi sebagian semen terhadap kuat tekan pada beton normal. Variasi campuran yang digunakan adalah bottom ash sebesar 10% dari berat semen dengan variasi penambahan red mud sebesar 0%, 5%, 10%, dan 15%. Hasil penelitian menunjukkan bahwa penambahan red mud dan bottom ash berpengaruh terhadap kuat tekan beton normal, dimana variasi campuran optimum diperoleh pada penggunaan bottom ash 10% dan red mud 5% yang menghasilkan nilai kuat tekan tertinggi dibandingkan variasi lainnya.
References
[1] A. Adlimi, Hermansyah, and Adi Mawardin, “PEMANFAATAN LIMBAH FLY ASH DAN BOTTOM ASH SEBAGAI BAHAN TAMBAH DAN BAHAN PENGGANTI UNTUK MENINGKATKAN NILAI KUAT TEKAN BETON,” Hexagon Jurnal Teknik dan Sains, vol. 6, no. 2, pp. 103–113, Jun. 2025, doi: 10.36761/hexagon.v6i2.4529.
[2] H. Harjunan, I. Lakawa, H. Hujiyanto, and V. A. Ilham, “Pengaruh Penambahan Bottom Ash Dan Fly Ash Sebagai Bahan Subtitusi Campuran Beton,” Sultra Civil Engineering Journal, vol. 4, no. 2, pp. 133–139, Oct. 2023, doi: 10.54297/sciej.v4i2.526.
[3] K. Ester Ghozali, A. Yonathan, A. Antoni, and D. Hardjito, “PENELITIAN AWAL PEMANFAATAN FLY ASH DAN BOTTOM ASH PLTU SURALAYA DALAM PEMBUATAN BETON DI LINGKUNGAN PANTAI,” Feb. 2019.
[4] M. Qomaruddin, Y. A. Saputro, and S. Sudarno, “KAJIAN PENGGUNAAN BOTTOM ASH SEBAGAI MORTAR BETON,” Prosiding Sains Nasional dan Teknologi, vol. 1, no. 1, Aug. 2018, doi: 10.36499/psnst.v1i1.2253.
[5] M. A. Bastian, M. Y. M. Making, and A. P. Koten, “Pemanfaatan Limbah Bottom Ash Pltu Timor-1 Sebagai Bahan Pengganti Agregat Halus Dalam Pembuatan Beton,” Syntax Literate ; Jurnal Ilmiah Indonesia, vol. 11, no. 2, pp. 1569–1577, Feb. 2026, doi: 10.36418/syntax-literate.v11i2.63936.
[6] Hardiana, N. Junus, and P. Mushar, “Bottom Ash: Pengganti Agregat Halus dalam Pembuatan Beton,” Jurnal Lingkungan Binaan Indonesia, vol. 8, no. 3, pp. 105–111, Sep. 2019, doi: 10.32315/jlbi.8.2.109.
[7] H. Harjunan, I. Lakawa, H. Hujiyanto, and V. A. Ilham, “Pengaruh Penambahan Bottom Ash Dan Fly Ash Sebagai Bahan Subtitusi Campuran Beton,” Sultra Civil Engineering Journal, vol. 4, no. 2, pp. 133–139, Oct. 2023, doi: 10.54297/sciej.v4i2.526.
[8] D. Agustiya, K. Hidayanti, and E. Rusmita, “PENGARUH PENAMBAHAN BOTTOM ASH SEBAGAI BAHAN CAMPURAN AGREGAT HALUS TERHADAP KUAT TEKAN BETON,” Sep. 2024.
[9] M. Alosta et al., “Properties and Microstructure of Treated Coal Bottom Ash as Cement Concrete Replacement,” Civil Engineering Journal (Iran), vol. 10, no. 4, pp. 1125–1144, Apr. 2024, doi: 10.28991/CEJ-2024-010-04-08.
[10] B. M. Chairullah and H. Yunita, “Pengaruh Penambahan Bottom Ash Terhadap Parameter Kuat Geser Tanah Lempung Desa Beureugang Kaway XVI Aceh Barat,” Journal of The Civil Engineering Student, vol. 3, no. 2, pp. 106–112, 2021.
[11] C. Venkatesh, R. Nerella, and M. S. R. Chand, “Role of red mud as a cementing material in concrete: a comprehensive study on durability behavior,” Innovative Infrastructure Solutions, vol. 6, no. 1, p. 13, Mar. 2021, doi: 10.1007/s41062-020-00371-2.
[12] W. Rosasalina, T. A. Zaharah, and I. H. SIlalahi, “KOMPOSISI UNSUR DAN KARAKTERISASI MINERAL MAGNETIK DALAM RED MUD, RESIDU BAUKSIT DI PT. INDONESIA CHEMICAL ALUMINA (ICA) KALIMANTAN BARAT,” 2021, Accessed: Oct. 31, 2024. [Online]. Available: http://jurnal.untan.ac.id/index.php/IJoPAC
[13] S. U. Dewi and F. Prasetyo, “ANALISA PENAMBAHAN BOTTOM ASH TERHADAP KUAT TEKAN DAN KUAT TARIK BELAH BETON,” Jul. 2021.
[14] M. Ir. Bambang Sujatmiko, TEKNOLOGI BETON DAN BAHAN BANGUNAN. CENDEKIA,MEDIAA SAHABAT, 2019.
[15] K. W. Wardhani, E. K. Pangestuti, R. Kusumawardani, and M. A. Firdaus, “PEMANFAATAN FLY ASH DAN BOTTOM ASH PLTU REMBANG UNTUK PEMBUATAN BETON MENGGUNAKAN SEMEN PPC,” Jurnal Inovasi Konstruksi, vol. 3, no. 1, pp. 35–45, Apr. 2024, doi: 10.56911/jik.v3i1.86.